- 銳鈦礦相納米TiO2anatase nano-TiO2
- 銳鈦礦相TiO2anatase TiO2
- 05%的摻鐵納米二氧化鈦為銳鈦礦型、粒徑為63.4nm、比表面積為82.2m~2/g的球形粒子。On the other hand, the particle size is 63.4nm and the surface area is 82.2 m2/g from the sample of 0.05%25 iron-doped anatase titania calcined at the same temperature.
- 銳鈦礦相TiO2（101）表面TiO2 anatase (101) surface
- 銳鈦礦相anatase
- 雙相納米填料diphase nano-filler
- 開(kāi)放水熱法制備莫來(lái)石復相納米晶體的影響因素EFFECTIVE FACTORS IN PREPARATION FOR MULTI-PHASE MULLITE NANOCRYSTALS BY THE NORMAL PRESSURE OPEN-SYSTEM HYDRO-THERMAL REACTION
- 在納米TiO2中復合SiO2能有效抑制銳鈦礦向金紅石的轉變,增加銳鈦礦的穩定性,并阻止TiO2晶粒的聚集生長(cháng).The average size of titania decreased from 38.4 nm in pure TiO2 to 3.9 nm in SiO2/TiO2 with a SiO2/TiO2 molar ratio of 2/1. In addition, the photocatalytic activity decreased with the increase of rutile content.
- 各向同性雙相納米晶粘結磁體制備工藝的改進(jìn)對矯頑力影響Dual-phase Nanocrystalline Isotropy Bonded Magnets was Ameliorated by Preparation Technology for Influence of Coercivity
- 銳鈦礦anatase
- 鈦礦titanium ore
- 改進(jìn)的檸檬酸鹽溶膠-凝膠法制備四方相納米尺寸鈦酸鋇粉體Preparation of Nanometer Crystalloid Barium Titanate Powder by Improved Citrate Sol-Gel Method
- 工業(yè)級銳鈦型TiO2commercial anatase TiO2
- 板鈦礦pyromelane
- 砂鈦礦Titaniferous placer
- 銳鈦型納米二氧化鈦anatase nanometer titanium dioxide
- 鎂鈦礦dauphinite
- 鉛鈦礦macedonite
- 以主波長(cháng)254nm的紫外燈作為光源 ,研究了銳鈦型納米TiO2 對鄰硝基苯酚、2,4_二硝基苯酚的光催化降解行為 ,并與普通TiO2 作了對比;Nanosized titania(TiO2) with particle size less than 10 nm has been prepared by low _ temperature thermolysis. The photocatalytic degradation of o _ nitrophenol and 2,4 _ dinitrophenol with prepared TiO2 was studied using UV light source at 254 nm.
- 釷鈦礦thorutite