It was concluded that while nano - Al2O3/carbon black mass ratio was 1/1, tensile strength and tear strength were best, nano - Al2O3/ carbon black mass ratio was 3/1, abrasive resistance and fatigue resistance were the best.
英
美
- 結果表明,當Al2O3/炭黑質(zhì)量比為1/1時(shí),天然橡膠硫化膠的拉伸強度和撕裂強度最高,當Al2O3/炭黑質(zhì)量比為3/1時(shí),天然橡膠硫化膠的耐磨性和耐疲勞性能最佳。